PENGARUH ORIENTASI SERAT DAN WAKTU ALKALISASI PADA LAMINATES COMPOSITE POLYESTER-SERAT BEMBAN (DONAX CANNIFORMIS) TERHADAP KEKUATAN BENDING, IMPACT DAN BENTUK PATAHAN

Akhmad Syarief, Achmad Azhar Basyir, Andy Nugraha Andy Nugraha

Abstract


Plant Bemban (Donax canniformis) is one of the plants that is often found in the swamp area of South Kalimantan that grows wildly on the roadside and around the home garden. The purpose of this study is to find out how large the bending strength and composite impact is reinforced with bemban fiber with polyester matrix with variations in fiber orientation and alkalization time. The method is done by alkalizing the banana fiber with 4% NaOH solution with a variation of 30 minutes, 60 minutes and 90 minutes. The process of making composites with 3 layers varies the direction of fiber A (0°,45°,90°), B (45°,90°,0°), C (90°,45°,0°) and the method used is how to hand lay up. Broken photos after testing using macro photo observations. The results showed that the specimens with the highest immersion time of 30 minutes for bending with variations A (0°,45°,90°) of 112.24 MPa and the lowest at 60 minutes with variation C (90°,45°,0°) amounting to 12.67 MPa. Price impact (HI) is highest at 60 minutes immersion time with variations A (0°,45°,90°) of 0.0208 joule/mm2 and the lowest at 30 minutes immersion time with variation C (90°,45°,0°) of 0.0115 joules/mm2.

Keywords


Composite, Bemban, Fiber Orientation, Alkalization Time

Full Text:

PDF

References


ASTM. D 790 standard test methods for flexural properties of unreinforced and reinforced plastics and electrical insulating material. Philadelphia, PA : American Society for Testing and Materials.

ASTM D256-00, Standard Test Methods for Determining the Izod Pendulum Impact Resistance of Plastic.

Badan Pusat Statistik Provinsi Kalimantan Selatan. (2014). Kalimantan Selatan dalam Angka. Badan Pusat Statistik Provinsi Kalimantan Selatan, Banjarmasin.

Bledzki, AK, Reihmane S, Gassan J. (1996). J Appl Polym Sci1 1996: 1329-1336.

Callister, W. D. (1991). Material Science and Engineering an Introduction, John Willey and Sons Inc, New York.

Imra, Iswandi., (2009). Pengaruh Proses Vakum Dan Variasi Tekanan Terhadap Kekuatan Tarik Komposit Serat Alam (Coir Fiber Reinforced Resin Composite). Tugas akhir, Jurusan Teknik Mesin, ,Fakultas Teknik, Universitas Andalas, Padang.

Jones, M. R., (1999). Mechanics of Composite Material , Mc Graw-hill Kogakusha, Ltd.

Jacob J.A., Kilduft T.K. (1994). Engineering Material Technology Structure, Processing, Property andSelection 2. Prentice Hall, Inc A Simon and Schuster Company, USA.

KAW. K Autar (2006).Mechanics of Composite Material 2nd ed, Taylor & Francis Group, New York.

M. Jacob, K.T. Varughese, S. Thomas. (1994). Novel woven sisal fabric reinforced natural rubber composite: tensile and swelling characteristics, Journal of Composite Material

Neagu Cristean, Dkk. (2007). Stiffnes Contribution Of Wood Fibers To Composite Material. KHT Solid Mechanic.

Smith, W.F. (1996). Priciples of Material Science and Engineering 2nd ed, Mc Graw-hill, Singapore.

Schwartz, Mel M. (1984). Composite Material Handbook Vol I, Polymer Matrix Composites Guidelines For Characterization Of Structural Materials, Mc Graw Hill Companies, Inc.

Soemardi, Tresna P. Kusumaningsih, Widjajalaksmi. Irawan, Agustinus Purna. 2009. Karakteristik Mekanik Komposit Lamina Serat Rami Epoksi Sebagai Bahan Alternatif Soket Prostesis. Universitas Indonesia. Depok.

Timing SL.R. 1998. Engineering Material Adisson Wesley Iongman Limited.

Widodo, B., 2007. Analisis Sifat Mekanik Komposit Epoksi Dengan Penguat Serat Pohon Aren (Ijuk) Model Lamina Berorientasi Sudut Acak (Random). Institut Teknologi Nasional. Malang.




DOI: http://dx.doi.org/10.20527/infotek.v22i2.12387

Article Metrics

Abstract view : 421 times
PDF - 383 times

Refbacks

  • There are currently no refbacks.


Copyright (c) 2022 INFO-TEKNIK