PENGARUH MEDIA PENDINGIN DAN WAKTU TUNGGU TERHADAP POROSITAS, KEKERASAN DAN STRUKTUR MIKRO MATERIAL AL PADUAN (RONGSOKAN) MENGGUNAKAN METODE PENGECORAN EVAPORATIVE

Komang Aria Kresna Kepakisan, Rudi Siswanto

Abstract


The purpose of this research is to know the effect of cooling media and holding time to porosity, hardness and micro structure of Al alloy material (scrap) using evaporative casting method. The method used in this research is the experimental method of smelting Al Alloy piston scrap and poured at 700°C in Styrofoam pattern mold with 10 and 15 minutes holding time, then cooled with medium air, brine, and water of PDAM for 30 minutes. The material used is excavator aluminum alloy (scrap) izumi piston with silicon aluminum alloy (Al-12% Si). The highest hardness value obtained from the results of cooling casting with the brine cooling medium for 10 minutes that is equal to 217,996 kg / mm2 average HV. At porosity, the highest value was obtained at holding time of 15 minutes with PDAM water cooling medium 5.088% against raw material. While the result of visual observation with 50x magnification of microstructure of specimen to raw material, Si material in raw material has significant length increase. The conclusion of the research results is that re-casting with variations of cooling medium and waiting time will increase hardness and increase porosity, except on brine cooling medium.

 

Keywords: MTTR, MTTF, RCM (Reliability Centered Maintanance)

Full Text:

PDF

References


Ashar L. H., Purwanto H., Respati S. M. B., 2012 “Analisis Pengaruh Model Sistem Saluran Dengan Pola Styrofoam Terhadap Sifat Fisis dan Kekerasan Produk Puli Pada Proses Pengecoran Aluminium Daur Ulang”, MOMENTUM, Vol. 8 1, April Fakultas Teknik Universitas Wahid Hasyim Semarang, pp 48-55

ASM International. All Rights Reserved Aluminum-Silicon Casting Alloys: Atlas Microfractographs, 2004

Norhadi, 2010, “Studi Karakteristik Material Piston dan Pengembangan Prototipe Piston Berbasis Limbah Piston Bekas”, Program Studi Magister Teknik Mesin Universitas Diponegoro Semarang

Nuraini E., Martoyo, Sigit, 1996, “Pengaruh Suhu dan Media Pendingin Terhadap Perubahan Kekerasan dan Struktur Mikro pada Perlakuan Panas AlMg2”, Prosiding Pertemuan dan Presentasi Ilmiah PPNY-BATAN 1996 PEBN-BATAN, Komplek Puspitek Serpong, Tangerang.

Roziqin K., Purwanto H., Syafa’at I., 2012, “Pengaruh Model Sistem Saluran pada Proses Pengecoran Aluminium Daur Ulang terhadap Struktur Mikro dan Kekerasan Coran Pulli Diameter 76 mm dengan Cetakan Pasir”, MOMENTUM, Vol. 8, No. 1, April Fakultas Teknik Universitas Wahid Hasyim Semarang, pp 33-39

Septianto B. A. dan Setiyorini Y., 2013, “Pengaruh Media Pendingin pada Heat Treatment terhadap Struktur Mikro da Sifat Mekanik Friction Wedge AISI 1340”, Jurnal Teknik POMITS, Vol. 2, No. 2, (2013) Institut Teknologi Sepuluh Nopember (ITS), ISSN: 2337-3539, pp 342-347

Siswanto R., 2015, “Analisis Struktur Mikro Paduan Al-19, 6Si-2,5Cu, 2,3Zn (Scrap) Hasil Pengecoran Evaporative”, Proceeding Seminar Nasional Tahunan Teknik Mesin XIV (SNTTM XIV) 7-8 Oktober Akademi Teknik Pembangunan Nasional Banjarbaru

Supriyanto, 2009, “Analisis Hasil Pengecoran Aluminium dengan Variasi Media Pendinginan”, JANATEKNIKA Vol. 11, No. 2, Juli, ISSN: 1441-1152

Surdia, T. dan Cijiiwa K, 1991, Teknik Pengecoran Logam, PT Pradnya Paramita, Jakarta




DOI: https://doi.org/10.20527/jtam_rotary.v1i1.1397

Refbacks

  • There are currently no refbacks.


JTAM ROTARY

Editorial Address

Department of Mechanical Engineering, Engineering Faculty, Lambung Mangkurat University

Jl. Jenderal Achmad Yani Km. 35,5 Banjarbaru Telp. (0511)-4773858 Fax. 0511-4773858.

HP: 0853-3262-2556 (Andy Nugraha) 

E-mail: j[email protected], [email protected]

Home Page: http://bit.ly/JurnalRotary

Lisensi Creative Commons
JTAM ROTARY Under License Creative Commons Atribusi 4.0 Internasional. Department of Mechanical Engineering, Engineering Faculty,  Universitas Lambung Mangkurat