PENGARUH VARIASI SUHU DAN MEDIA PENDINGIN PADA PROSES PACK NITRIDING MATERIAL SUS 630 TERHADAP NILAI KEKERASAN DAN STRUKUR MIKRO

YOSEPH NETANYAHU SILALAHI, Mastiadi Tamjidilllah

Abstract


This research investigates the application of material engineering techniques on Stainless steel SUS 630 so that it not only has good resilience and resistance to corrosive properties but also has hard properties on its surface. In an effort to improve the quality of violence on the surface, among others, by surface hardening technique, one of which is a heat treatment technique by adding nitrogen elements to the surface of a material called the nitriding pack process. The nitrogen source in the pack nitriding process comes from urea (CO(NH2)2) with a nitrogen content of 46%. Parameters for controlling this study using variables by applying temperature variations (4200C, 4700C, 5200C, 5700C, 6200C)  and cooling media (inside the furnace, room temperature, and with fan) with a holding time of 2 hours. To evaluate this study microstructure testing, diffusion layer testing and micro hardness testing were carried out. From the results of the test it was found that there was no significant transformation of the microstructure shape when comparing with raw material, the optimal value of diffusion layer was in the cooling furnace with a temperature of 6200C with an average of 4.57 μm and white layer 0.53 , the highest hardness was at 6200C with cooling in furnace media which has a value of 80.9 HRN.


Keywords


Nitriding; Stainless Steel SUS 630; Kekerasan; Struktur Mikro; Difusi

Full Text:

PDF

References


ASM Internasional, 1991, “ Metals Handbook Heat Treating”, Volume 4.

Bakran, Fachmi Hasan . (2011). Pengaruh Nitridasi terhadap Laju Korosi pada Baja KS01. Tugas Akhir Sarjana S-1, Departemen Matematika dan Ilmu Pengetahuan Alam, Program Studi Fisika IPB, Bogor.

Metallography, Structures, and Phase Diagrams, Vol 8, Metals Handbook, 8th ed., American Society for Metals, 1973.

Priyantoro, D., Sujitno, T., & Utami, R. A. Pengerasan Permukaan Bearing Dengan Teknik Plasma Nitriding.

Purwadadi, W., Idamayanti, D., & Firman, F. (2017). Peningkatan Kekerasan Permukaan Ferro Casting Ductile (Fcd) 700 Melalui Proses Nitridasi Dengan Media Urea. Creative Research Journal, 1(01), 64-78.

Rahayu, S. (2017). Pengaruh Proses Powder Nitriding Terhadap Perubahan Kekerasan Dan Tebal Lapisan Difusi Pada Pahat Bubut High Speed Steel (Doctoral dissertation, Universitas Pendidikan Indonesia).

Rumendi, U., & Hermawan, H. (2014). Analisis Pengerasan Permukaan Dan Struktur Mikro Baja AISI 1045 Melalui Proses Nitridasi Menggunakan Media Urea. Jurnal konversi energi dan manufaktur UNJ, 1(2), 104-109.

Sulistyo, E., Setyarini, P. H., & Sudana, Y. (2010). Proses Pack Nitriding dengan Variasi Suhu dan Media Pupuk Nitrogen Terhadap Kekerasan AISI 420. Rekayasa Mesin,(1), 17-20.

Thelning, K.E. (1984). Steel and its Heat Treatment, 2 ed. Jordan Hill : Butterworth-Heinemann.

Totten, G. (2004). Handbook of Metallurgical Process Design (Materials Engineering). 1st ed. CRC Press.




DOI: https://doi.org/10.20527/jtam_rotary.v3i1.3429

Refbacks

  • There are currently no refbacks.


JTAM ROTARY

Editorial Address

Department of Mechanical Engineering, Engineering Faculty, Lambung Mangkurat University

Jl. Jenderal Achmad Yani Km. 35,5 Banjarbaru Telp. (0511)-4773858 Fax. 0511-4773858.

HP: 0853-3262-2556 (Andy Nugraha) and 0821-5232-0035 (Herry Irawansyah)

E-mail: j[email protected], [email protected], [email protected]

Home Page: http://bit.ly/JurnalRotary

Lisensi Creative Commons
JTAM ROTARY di bawah Lisensi Creative Commons Atribusi 4.0 Internasional.Department of Mechanical Engineering, Engineering Faculty,  Universitas Lambung Mangkurat