PENGARUH KATALIS ASAM SULFAT PADA SINTESIS NITROSELULOSA TERHADAP DERAJAT SUBSTITUSI

Fitriannoor Fitriannoor, Taufiqur Rohman Taufiqur Rohman, Mahmud Mahmud

Abstract


Effect of sulfuric acid as catalyst due to synthesis of nitrocellulose from pure cellulose towards substitusion degree had been done. The purpose of this research are to find FT-IR absorbance and substitution degree. Nitrocellulose wassynthesized using nitration method in a mixture nitric acid, sulfuric acid and water then cooled at 5OC - 15OC for 60 minutes. Results is showed that nitrocellulose synthesized has FT-IR character that the formation nitro functional group (-NO2) sharp peak at 1635 cm-1 were subtituted completely.  However the peak at 1361 cm-1 and 1288 cm-1 nitro functional group (-NO2) incompletely substituted because peak is not sharp.  So two hydroxyl functional group peak (-OH) at 3201 cm-1 and 3424 cm-1. Concluded, substitution degree using absorbance ratio from FT-IR spectrum is 2,89.


Full Text:

PDF

References


DAFTAR PUSTAKA

Ahmad, A. L., S. C. Low, S. R. A. Shukor, & A. Ismail. 2008. Synthesis and Characterization of Polymeric Nitrocellulose Membrane: Influence of Additive and Pore Formers on the Membran Morphology. Journal of Applied Polymer Science 108: 2550-2557.

Apriani, R., T. Rohman, & K. Mustikasari. 2018. Sintesis dan Karakterisasi Membran Selulosa Asetat dari Tandan Kosong Kelapa Sawit. Jurnal Riset Industri Hasil Hutan (9)2: 91-98.

Cheung C., 2011. Studies of The Nitration of Nitrocellulose – Application in New Membrane Materials.Thesis Master of Science. The university of British Columbia. Vancouver.

Desriani, R., Padil, & Yelmida. 2012. Proses Pembuatan Nitroselulosa dari Limbah Pelepah Sawit. Jurnal Laboratorium Kimia Organik 1: 1-12.

Eriningsih, R., R. Yuliana, & T. Mutia. 2012 Pembuatan Karboksimetil Selulosa dari Limbah Tongkol Jagung untuk Pengental pada Proses Pencapan Tekstil. Jurnal Balai Besar Tekstil. 26: 105-113.

Erlangga P. B., I. Tafdhila, Mahfud, & Rr. P. Prihatini. 2012. Pembuatan Nitroselulosa dari Kapas (Gossypium Sp.) dan Kapuk (Ceiba Pentandra) Melalui Reaksi Nitrasi. Jurnal Teknik ITS. 1: 41-46.

Fitriannoor, T. Rohman, & Mahmud, 2020. Sintesis Nitroselulosa

dari Selulosa Murni Menggunakan Asam Sulfat sebagai Katalis (Skripsi). Universitas Lambung Mangkurat. Banjarbaru.

Hartaya, K. 2010. Korelasi Kadar Nitrogen Dalam Nitroselulosa. Majalah Sains dan Teknologi Dirgantara. 5:74-75.

Heize, T., 2015. Cellulose: Structure and Properties. Springer International Publishing Switzerland. Switzerland.

Miranda, Padil, & Yelmida,. 2009. Pembuatan Nitroselulosa dari Selulosa – α Limbah Pelepah Sawit dengan variasi Waktu Nitrasi dan Rasio Bahan Baku Terhadap Asam Penitrasi. Jurusan Teknik Kimia Universitas Riau, Pekanbaru.

Rahman. M. F., I M. J. Astika, Y.D. Kurniawan, & Suratmo. 2011. Pengaruh Waktu Nitrasi dan Penggunaan Gelombang Ultrasonik Terhadap Persentase Mol Nitrogen Dalam Nitroselulose Hasil Sintesis

Berbahan Dasar Serat Kapas. Jurnal Natural B. 2(1): 159-167

Saragih, E, Padil, & Yelmida. 2009. Pembuatan Nitroselulosa dari Selulosa Hasil Pemurnian Pelepah Sawit dengan Hidrogen Poroksida (H2O2) Sebagai Bahan Pembuatan Propelan. Jurnal Teknik Kimia Universitas Riau. 1.

Stovbun, S. V.,S. N. Nikol’skiia, V. P. Mel’nikova, M. G. Mikhalevaa, Ya. A. Litvina, A. N. Shchegolikhina, D. V. Zlenkoa, V. A. Tverdislova, D. S. Gerasimovb, & A. D. Rogozinb. 2016. Chemical Phycics of Nitration. Semenov Institute of Chemical Physics, Russian Academy of Science. Moscow, Russia.

Wade, L.G. JR. 2013.Organic Chemistry Eighth Edition. Pearson. Glenwiew.




DOI: https://doi.org/10.20527/jns.v2i2.6671

Refbacks

  • There are currently no refbacks.


Lisensi Creative Commons

Ciptaan disebarluaskan di bawah Lisensi Creative Commons Atribusi 4.0 Internasional.

Diterbitkan oleh FMIPA Universitas Lambung Mangkurat