SIFAT PAPAN PARTIKEL DARI LIMBAH KAYU GELAM (Melaleuca cajuputi) PADA BERBAGAI KADAR PEREKAT PVAC
Abstract
ABSTRACT. The research aim to analyze physical and mechanical properties of particle board from gelam wood waste which is influenced by PVAc adhesive, and this research is useful to provide information on the use of gelam wood waste through the manufacture of particle board products using PVAc adhesive with various adhesive grades. The research design which is applicated, is Completely Randomized Design (RAL) with 4 treatments and 3 repetition, so it has 12 boards as its sample. The parameters that I calculate in this research are moisture content, density and firmness (MoR). The results of the research explained the values of each parameter are: moisture content 14.94% - 16.35%, density 0.74g / cm3 - 0.85g / cm3 and bending firmness (MoR) 3,31kg / cm3 - 14, 28kg / cm3. Thus the particle board density meets the standards of SNI 03-2105-2006 and JIS A 5803.
Keywords: Gelam; PVAc; Particle Board.
ABSTRAK. Penelitian ini bertujuan untuk menganalisis sifat fisik dan mekanik papan partikel berbahan limbah kayu gelam yang dipengaruhi oleh kadar perekat PVAc, dan penelitian ini bermanfaat untuk memberikan informasi penggunaan limbah kayu gelam melalui pembuatan produk papan partikel dengan berbagai kadar perekat PVAc. Rancangan penelitian yang dipakai adalah Rancangan Acak Lengkap (RAL) yang menerapkan 4 perlakuan serta 3 pengulangan, sehingga total sampel berjumlah 12 papan. Parameter yang saya hitung yaitu kadar air, kerapatan dan keteguhan lentur (MoR).
Hasil uji menunjukkan nilai masing-masing parameter yaitu: kadar air 14,94% - 16,35%, kerapatan 0,74g/cm3 – 0,85g/cm3 dan keteguhan lentur(MoR) 3,31kg/cm3 – 14,28kg/cm3 . Jadi, kerapatan papan partikel yang diuji telah memenuhi standar SNI 03-2105-2006 dan JIS A 5803.
Kata kunci: Gelam; PVAc; Papan Partikel
Full Text:
PDFReferences
Arifin, Y. F.,S. Hamidah, and Y.F. Arifin. 2014. The Analysis of Management and Timber Tread System of Gelam (Melaleuca cajuputi) from Peat Swamp Forest in South Kalimantan. Journal Wetlands Environmental Management Vol 2, No. 2, August 2014, ISSN 2354-5844.
Altinok, M., Tas, H.H., & Çimen, M. 2009 . Effects of Combined Usage of Traditional Glue Joint Methods in Box Construction on Strength of Furniture. Merial and desains. Vol 30-339
Alghifari, A.F. 2008. Pengaruh Kadar Resin Perekat Urea Formaldehida terhadap Sifat-Sifat Papan Partikel dari Ampas Tebu. Skripsi Mahasiswa Fakultas Kehutanan IPB.
Aini, Nurul S, K. Bintani dan A. Haris. 2008. Papan Partikel dari Pelepah Kelapa Sawit. Universitas Wijaya Mukti. Bandung
Arifin, Y.F., S.Hamidah, and Y.F. Arifin. 2016. Ecological Analysis of Gelam (Melaleuca cajuputi) on Peatland in South Kalimantan. Journal of Tropical Silviculture Science and Technology Vol 07 No.03 Suplemen, Desember 2016. ISSN: 2086-8227
Arifin, Y. F.,S. Hamidah, and Y.F. Arifin. 2017. SIte Analysis and Conservation of Gelam (Melaleuca cajuputi) on Peat Swamp Forest in South Kalimantan, Indonesia. IJRDO-Journal of Biological Science. Vol 3, Issue-3, March 2017, Paper-1. ISSN 2455-7676.
Bowyer JL, Shmulsky, Haygreen JG. 2003. Forest Products and Wood Science – An Introduction, Fourth edition. Iowa State University Press
Bowyer JL, Shmulsky R, dan Haygreen JG. 2003. Forest Product and Wood Science. USA:
Blackwell Publishing Professional.
Hamidah, S., and Y.F. Arifin. 2016. The Ability of Gelam (Melaleuca cajuputi) Wood Vinegar as A Coagulant Latex. Makalah dipresentasikan pada Seminar Internasional INOVCOM-FP 2016 “The 1st International Conference on Innovation and Comercialization of Forest Product”, 22 November 2016. Banjarbaru, Indonesia.
Hamidah, S., Y.F. Arifin, L. Wardani, D. Subari, and I.M. Sulastiningsih. 2016. The Properties of Particleboard Made of Bambo Mayan (Gigantochoa robusta) and Wood Waste Galam (Melaleuca cajuputi) . Makalah dipresentasikan pada Seminar Internasional INOVCOM-FP 2016 “The 1st International Conference on Innovation and Comercialization of Forest Product”, 22 November 2016. Banjarbaru, Indonesia.
Iswanto A H., 2008. Pengujian Siklis Papan partikel. Fakultas Pertanian. Universitas Sumatra Utara. Sumatra.
Jamaludin, K., Zaidon, A.A., Latif M., & Mohd N. (2001). Properties of particleboard manufactured from commonly utilized malaysian bamboo (Gigantochloa scortechinii). Pertanika J. Trap.Agric. Sci, 24 (2),151 - 157.
Junaidi, A.B., dan Rahmat Yunus. 2009. Kajian Potensi Tumbuhan Gelam (Melaleuca cajuputi Powell) untuk Bahan Baku Industri Pulp: Aspek Kandungan Kimia Kayu. Jurnal Hutan Tropis Borneo. Volume 10. No. 28 Edisi Desember 2009.
Lazuardi, D. Dan Supriadi, R. 2000. Teknik Pengelolaan Hutan Gelam Rakyat di Kalimantan Selatan (management technique of gelam forest in South Kalimantan). Laporan Hasil Penelitian (report of research). Balai Technologi Reboisasi. Departemen Kehutanan. BPPKP Banjarbaru. Unpublished.
Maloney, T. M. 1993. Modern Particleboard and Dry Process Fiberboard Manufacturing. Miller Fremann, Inc. San Francisco. USA.
Mujtahid. 2010. Pengaruh Ukuran Serbuk Aren Terhadap Kekuatan Bending, Densitas Dan Hambatan Panas Komposit Semen-Serbuk Aren (Arenga Pinnata). Fakultas Teknik. Surakarta: Universitas Sebelas Maret.
Oroh J., Sapupu F. P., Lumintang R., 2013. Analisis Sifat Mekanik Material Komposit Dari Serat Sabut Kelapa. Fakultas Teknik. Universitas Sam Ratulangi Manado.
Pamungkas, E. A. 2006. Kualitas Papan Partikel Limbah Dan Likuida Sabut Kelapa Dengan Fortifikasi Melamin Formaldehida. Skripsi. Fakultas Kehutanan. IPB. Bogor.
Putra, BE. 2009. Pengaruh Kadar Perekat Urea Formaldehyde Terhadap Sifat Fisis dan Mekanis Plafon Papan dari Sabut Kelapa. Skripsi. Universitas Andalas. Padang
Prayitno, T.A.,Wirnasari dan Sriyanti, D. 2014. Pengaruh Shelling Ratio dan Jumlah Perekat Urea Formaldehida terhadap Sifat Papan Serutan Bambu Petung (Dendrocalamus asper Backer). UGM. Yogyakarta
Roihan, A., R. Hartono, dan T. Sucipto. 2016. Kualitas Papan Partikel dari Komposisi Partikel Batang Kelapa Sawit dan Mahoni dengan Berbagai Variasi Kadar Perekat Phenol Formaldehida. Diakses dari http://download.portalgaruda.org/
Sandi, T. R., Karyadi, dan E. Setyawan. 2009. Pengaruh pPenambahan Serat Anyaman Bambu dengan Berbagai Variasi Jarak Terhadap Kuat Lentur, Tekan, dan Tarik Papan Partikel dari Serbuk Gergajian Kayu Sengon. Universitas Negeri Malang. Malang
Setyanto, R. H. ., I. Priyadithama, dan N. Maharani. 2011. Pengaruh Faktor Jenis Kertas, Kerapatan dan Presentase Perekat terhadap Kekuatan Bending Komposit Panel Serap Bunyi Berbahan Dasar Limbah Kertas dan Serabut Kelapa. Performa (2011) Vol. 10, No. 2: 89 – 94
Sitanggang, J.P., T. Sucipto, I. Azhar. 2015. Pengaruh Kadar Perekat Urea Formaldehida Terhadap Kualitas Papan Partikel dari Kayu Gamal (Gliricidia sepium) (The Effect of Urea Formaldehyde Adhesive Content on Quality of Gamal Wood Particleboard(Gliricidia sepium)). Diakses dari http://download.portalgaruda.org/
Wulandari F.T, 2005. Sifat Fisika dan Mekanika Papan Serat Berkerapatan Sedang (MDF) Dari Sabut Kelapa Dan Limbah Kayu Campuran. Fakultas Kehutanan, Universitas Mulawarman. Samarinda.
Wulandari, F.T. 2012. Deskripsi Sifat Fisika dan Mekanika Papan Partikel Tangkai Daun Nipah (Nypa fructicans, Wurmb), Batang Bengle (Zingiber cassumunar, Roxb). Media Bina Ilmiah, 6. 10.16.
Wulandari, F. T. 2013. Produk Papan Komposit Dengan Pemanfaatan Limbah Non Kayu. Media Bina Ilmiah Volume 7/6Desember 2013. Prodi Kehutanan Faperta. UNRAM. Mataram.
DOI: https://doi.org/10.20527/jss.v2i2.1061
Refbacks
- There are currently no refbacks.
Jurnal Sylva Scienteae is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.