PENGARUH ORIENTASI SERAT PADA KOMPOSIT KAIN POLYPROPYLINE

Muhammad Ariyansah, Achmad Kusairi Samlawi

Abstract


The purpose of this research is to know the effect of fiber orientation variation on tensile strength and impact strength on polypropyline fabric composite. In this study the reinforcing materials used were polypropyline fabrics with variations of fiber orientation 0º:-45º:0 ; 0:45º:0º ; and 0º:90:0º using unsaturated polyester resin 108 as the matrix. Preparation by hand lay up, impact testing conducted with reference standard ASTM D5942-96 and tensile testing conducted with reference ASTM D638-03 standard. The test results showed that the variation with 0°:90°:0° orientation gave the best effect to the impact test and tensile test with the impact price of 128,66 Joule / cm² and tensile strength of 98,49 MPa.

 

Keywords: Polypropyline, Composite, Impact Strength, Tensile Strength

Full Text:

PDF

References


Callister William D. 2007. Material Science and Engineering an Introduction. John Willey and Sons Inc. New York.

Fahmi Hendriawan. Hermansyah, Harry. 2011. Pengaruh Orientasi Serat Pada Komposit Resin Polyester/ Serat Daun Nanas Terhadap Kekuatan Tarik. Jurnal Teknik Mesin Institut Teknologi Padang. Volume 1. No. 1.

M, Kumaresan., S, Sathish., and N, Karthi., 2015, Effect of Fiber Orientation on Mechanical Properties of Sisal Fiber Reinforced Epoxy Composites. Journal of Applied Science and Engineering, Vol. 18, No. 3.

Smith, W,F., 1996, Principles of Materials Science And Engineering 2nd edition, McGraw-Hill, Inc. New York.




DOI: https://doi.org/10.20527/jtam_rotary.v1i1.1399

Refbacks

  • There are currently no refbacks.


JTAM ROTARY

Editorial Address

Department of Mechanical Engineering, Engineering Faculty, Lambung Mangkurat University

Jl. Jenderal Achmad Yani Km. 35,5 Banjarbaru Telp. (0511)-4773858 Fax. 0511-4773858.

HP: 0853-3262-2556 (Andy Nugraha) 

E-mail: j[email protected], [email protected]

Home Page: http://bit.ly/JurnalRotary

Lisensi Creative Commons
JTAM ROTARY Under License Creative Commons Atribusi 4.0 Internasional. Department of Mechanical Engineering, Engineering Faculty,  Universitas Lambung Mangkurat