THE EFFECT OF STAINLESS STEEL WIRE IMMERSION IN COCONUT WATER TO RESILIENCE CHANGE

Dwiki Azhar, Diana Wibowo, Fajar Kusuma Dwi Kurniawan

Abstract


Background: Orthodontic treatment is used to repair malocclusion. It is divided into fix and removable orthodontic and mostly use wire for the treatment. The wire that used in orthodontic treatment is austentic stainless steel type 304. Drinks that has low pH, such as coconut water may affect the stainless steel wire resilience. Objective: To determine the resilience effect of orthodontic wire that immersed in coconut water. Methods: This research was true experimental research with pre test and post test control group design use simple random sampling consisted of 2 groups. Control group was saline solution and treatment group was coconut water. Each group had 11 samples. Ortodontic wire 0.06 mm was cut along 3 cm and scratched. Measurement of the resilience wire was conducted before immersion and after immersion for 13 hours with temperature 37oC. Result: The study showed that wire resilience on saline solution before immersion and after immersion was 17,60 gram/mm. Wire resilience on coconut water before immersion was 17,60 gram/mm and after immersion was 17,59 gram/mm. The results of Dependent T test was p=0.167 (p> 0.05) and the test results of Independent T  test was p=0.837 (p> 0.05). Conclusion: There is no effect of stainless steel orthodontic wire immersion in coconut water to the change of  resilience.

Keywords


coconut water, resilience, stainless steel orthodontic wire

Full Text:

PDF

References


Luther F dan Moon, Z.N. Orthodontic Retainers and Removable Appliances: Principles of Design and use 1st ed. New Jersey: Wiley-Blackwell; 2013. p. 3-24

Singh G. Textbook of Orthodontics. 2nd ed. New Delhi: Jaypee brothers; 2007. p. 3-328.

Yulita N, Kurniawan FKD, Wibowo D. Perbandingan suhu 37oC dan 45oC Terhadap Daya Lenting Kawat Ortodonti Stainless Steel. Jurnal Kedokteran Gigi Dentino. 2017; 1(1): 12.

Khatmakar A. Ideal Properties of Orthodontic Wires and their Clinical Implication. Journal of Dental and Medical Sciences IOSR. 2015; 14(1): 47-48.

Castro SM, Ponces MJ, Vasconcelos M, Pollmann MCF. Orthodontic Wires and its Corrosion the Specific Case of Stainless Steel and Beta Titanium. Journal of Dental Sciences. 2015; 10(1): 2-3.

Rakkala A. Compotition, Phase Structure, and Corrosion of Nickle-Free and Nickle-Containing Stainless Steel Orthodontic Wire. Disertasi. Milwaukee: Marquette University; 2014. p. 1-17.

Siwy CJ, Tandean LEN, Anindita PS. Uji Pelepasan Logam Kromium (Cr) dan Nikel (Ni) Beberapa Merek Bracket Stainless Steel dalam Cairan Saliva Artifisial. Jurnal e-GiGi. 2015; 3(2): 422-424

Bonde MM, Fatimawali, Anindita PS. Uji Pelepasan Ion Logam Nikel (Ni) dan Kromium (Cr) kawat ortodontik Stainless Steel yang direndam dalam air kelapa. Jurnal Ilmiah Farmasi Pharmacon. 2016; 5(4): 41-44.

Wirasatyawan I, Ardhana W, Karunia D. Pengaruh Penggunan Air Polisher dan Jenis Kawat Terhadap Daya Lenting Kawat Busur Ortodontik Setelah Direndam Dalam Saliva Buatan. Jurnal Kedokteran Gigi. 2015; 6(4): 347-351.

Yanuar SE, Sutrisno A. Minuman Probiotik dari Air Kelapa Muda Dengan Starter Bakteri Asam Laktat Lactobacillus casei. Jurnal Pangan dan Agroindustri. 2015; 3(3): 909-910.

Rukmana HR. Untung Berlipat Dari Budi Daya kelapa Yogyakarta: Lily Publisher; 2016. Hal. 16-46.

Kementrian Pertanian. Outlook Komoditi Kelapa. Pusat data dan sistem informasi pertanian sekertariat jendral kementrian pertanian. Jakarta. 2014. Hal. 1-16.

Sumarji. Studi Perbandingan Ketahanan Korosi Stainless Steel tipe SS 304 dan SS 201 Menggunakan Metode U-Bend Test Secara Siklik Dengan Variasi Suhu dan pH. Jurnal ROTOR. 2011; 4(1): 1-7.

Calderon JP, Diaz MC, Bravo VMS, Gomez LM. Corrosion Performance of Fe-Cr-Ni Alloys in Artificial Saliva and Mouthwash Solution. Bioinorganic Chemistry and Application. 2015; 15(1): 1-9.

Hedberg YS, Wallinder IO. Metal Release From Stainless Steel in Biological Environments: A review. Biointerphases. 2015; 11(1): 2-15.

Schmidt RH, Erickson DJ, Sims S, Wolff P. Characteristics of Food Contact Surface Material Stainless Steel. Food Protection. 2012; 32(10): 574-576.

Yuan, F. Corrosion Effects of Chlorides on Metal Pitting Corrosion. London: InTech; 2012. p. 139-158.

Loto RT. Corrosion Resistance of Austenitic Stainless Steel in Sulphuric Acid. Internarional Journal of Physical Sciences. 2012; 7(10): 1677-1688.

Donik C, Kocijan A. Comparison of the Corrosion Behavior of Austenitic Stainless Stell in Sea Water and in a 3,5% NaCl Solution. Material and Technology. 2014; 48(6): 937-939.

Gapsari F. Pengantar Korosi. Malang: UB Press; 2017. Hal. 46-48.

Kim JH, Kim BK, Kim DI, Choi PP, Raabe D, Yi KW. The Role of Grain Boundaries in the Initial Oxidation Behavior of Austenitic Stainless Steel Containing Alloyed Cu at 700oC for Advance Thermal Power Plant Applications. Corrosion Science. 2015; 96(2015): 52-53.

Prasad SK, Rao CS, Rao DN. A Review on Welding of AISI 304L Austenitic Stainless Steel. Journal Manufacture Science. 2014; 14(1): 1-11.

Bassioni G. Korin A, Salama A. Stainless Steel as a Source of Potential Hazard due to Metal Leaching into Beverages. International Journal Electrochem. 2015; 10(15): 3792-3793.

Fandem J. Deterioration of Stainless Steel Corrosion Resistance Due to Welding. Journal Material Science & Engineering. 2017; 6(2): 1-3.

Vaghani,M, Vasanwala SA, Desai AK. Stainless Steel As a Structural Material: State of Review. Journal of Enginering Research and Aplication. 2014; 4(3): 657-659.

Abdullah Z, Ismail A, Ahmad A. The Influence of Porosity on Corrosion Attack of Austenitic Stainless Steel. Journal of Physics. 2017; 914(1): 1-7.

Ardhy S, Gunawarman, Affi J. Perilaku Korosi Titanium Dalam Larutan Modifikasi Saliva Buatan Untuk Aplikasi Ortodontik. Jurnal Mekanikal. 2015; 6(2): 585-593.




DOI: http://dx.doi.org/10.20527/dentino.v3i2.5374

DOI (PDF): http://dx.doi.org/10.20527/dentino.v3i2.5374.g4534

Article Metrics

Abstract view : 1043 times
PDF - 323 times

Refbacks

  • There are currently no refbacks.


 

Contact Us:
Faculty of Dentistry
Lambung Mangkurat University
Jalan Veteran No. 128 B Banjarmasin, Indonesia
Telp/Fax. (0511) 3255444;

E-mail. fkg@ulm.ac.id / dentino.fkg@ulm.ac.id
Website. fkg.ulm.ac.id

 

Creative Commons License
This work is licensed under a Creative Commons Attribution 4.0 International License.